FEATURES OF 304 and 304L STAINLESS STEEL COIL:
1. SPECIFICATION:
1) Grade: AISI 304/SUS 304 / S30400 / 1.4301
2) Shape: Coil / Roll / Strip
3) Treatment: Hot Rolled and Cold Rolled
4) Surface: No.1 / 2B / No.4 / HL / Brushed / BA / 8K Mirror / Embossed / Etched etc. (With Paper or PVC film to protection)
5) Thickness Range:
0.3 - 3mm ( Cold Rolled Process )
3 - 12mm or more (Hot Rolled Process)
6) Edge: Slit edge & Mill edge
7) Width Range: 10 - 2000mm
8) Length Range: Coil or as your request
9) Standard Size:
1000mm x coil mm
1500mm x coil mm
4' ----------1220mm x coil mm
5' ----------1524mm x coil mm
Above is our normal size of 304 and 304L stainless steel coil, but are capable of shearing or custom leveling to your required lengths and widths.
10) Available Standard:
ASTM, AISI, SUS, JIS, EN, DIN, GB, ASME, etc.
In general, ASTM A240/A240M or as your requirements
11) Certification: MTC and SGS and Any third party inspection
12) Package: Standard Export Sea-Package (Waterproof Kraft Paper + Bundle with steel strip)
13) Brand: TISCO, BAO STEEL, BAOXIN, ZPSS, LISCO, JISCO, etc.( main mills)
14) Containers:
20ft GP:5898mm(Length)x2352mm(Width)x2393mm(High)
40ft GP:12032mm(Length)x2352mm(Width)x2393mm(High)
40ft HC:12032mm(Lengh)x2352mm(Width)x2698mm(High)
20' container load 25tons goods whose length is under 5.8m
40' container load 25tons goods whose length is under11.8m
2. TYPICAL APPLICATIONS:
Chemical equipment and piping, heat exchanger components, dairy and food handling equipment and utensils, cryogenic vessels and components, architectural and structural applications exposed to non-marine atmospheres
3. CHEMICAL COMPOSITION:
5. PROCESSING:
Types 304 and 304L cannot be hardened by thermal treatment. Annealing: Heat to 1850o F to 2050 o F and cool at sufficiently high rates through 1500oF to 800oF to avoid precipitation of chromium carbides. Stress Relief Annealing: Cold worked parts should be stress relieved at 750oF for ½ to 2 hours.
6. FORMING:
Annealed Types 304 and 304L can be fabricated by roll forming, deep drawing, bending and most other fabrication techniques. Due to the high work hardening rate of these materials, intermediate anneals maybe required to successfully fabricate the part.
7. WELDING:
Types 304 and 304L are weldable by most fusion or resistance welding techniques. If filler metal is required, Type 308 is normally used. Type 304L should be used in heavier sections to reduce the occurrence of carbide precipitation in the heat affected region adjacent to the weld pool
8. CORROSION:
Types 304 and 304L provides corrosion resistance in a wide range of moderately oxidizing and reducing conditions, fresh water and non-marine applications.